ZBLAN光纖是由ZrF4、BaF2、LaF3、AlF3和NaF等重金屬氟化物組成的復合玻璃光纖。與廣泛應用的石英光纖相比，ZBLAN光纖具有傳輸波長范圍寬（0.35μm~4μm）和摻雜稀土離子發(fā)射效率高等特點。通過開發(fā)一種獨te的光纖制造技術，筱曉光子推出低成本生產出高質量（特別是低損耗）的氟化物纖維。
400um大纖芯中遠紅外傳能光纖,400um大纖芯中遠紅外傳能光纖● 有效傳輸范圍從300nm到5500nm
● 出色的光譜均勻性
● 高激光損傷閾值
● 鈥和鉺激光傳輸?shù)睦硐脒x擇
● 高效率束的高包芯比
● 激光遙測光譜學
● 化學傳感
● 醫(yī)學診斷學
● 激光束傳輸
● FLIR
● 高溫計
| Item | ZSF-9/125-N-0.20 | Custom fiber |
| Fiber Type | Step Index | |
| Core Diameter (µm) | 9±1 | 2 ~ 12 |
| NA | 0.20±0.01 | 0.12, 0.16, 0.21, 0.26 |
| Cut-off Wavelength (µm) | <2.6 | - |
| Loss@1.5µm (dB/m) | <0.1 | |
| Cladding Diameter (µm) | 123±3 | |
| Coating Diameter (µm) | 460±30 | |
| Core/Cladding Glass | ZBLAN Fluoride Glass | |
| Coating Material | UV curable acrylate | |
| Proof Test | 1.25cm Radius | |
| Item | ZMF-400/500-N-0.27 | ZMF-160/200-N-0.27 | ZMF-100/125-N-0.27 | Custom fiber |
| Fiber type | Step Index | |||
| Core dia. (µm) | 400±25 | 160±10 | 95±5 | 60 ~ 800 |
| Cladding dia. (µm) | 500±25 | 200±10 | 123±5 | 80 ~ 1,000 |
| Coating dia. (µm) | 600±30 | 480±30 | 460±30 | 100~ 600 |
| NA | 0.27±0.01 | 0.22, 0.27, 0.30 | ||
| Loss@2.5µm (dB/m) | <0.1 | |||
| Core/cladding glass | ZBLAN fluoride glass | |||
| Coating material | UV curable acrylate | |||
| Proof test | 6cm radius | 2cm radius | 1.25cm radius | TBD |
| Item | RE doped Single Cladding Fiber | RE doped Double Cladding Fiber |
| Fiber type | Step index | |
| Dopant | Pr, Nd, Ho, Er, Dy, Tm, Yb, others | |
| Dopant concentration | 500~60,000 | |
| Core diameter (µm) | 2 ~ | |
| Core NA | 0.06, 0.12, 0.16, 0.21, 0.26 | |
| 1st Cladding diameter (µm) | 123±3 | 123, 200, 500 |
| 1st Cladding shape | Circular | Circular Octagonal Rectangular, etc. |
| 1st Cladding NA | N/A | > 0.5 |
| 2nd cladding thickness (µm) | N/A | >30 |
| 2nd cladding material | N/A | Fluoro-acrylate |
| Outer diameter (µm) | 460±30 | 460, 480, 600 |
| Core/Cladding glass | ZBLAN fluoride glass | |
| Coating material | UV curable acrylate | |
| Proof test | 1.25cm radius | TBD |